دانلود ترجمه مقاله ساختار و خواص رینک پیستون ساخته شده از چدن
ترجمه در قالب فایل Word و قابل ویرایش میباشد
سال انتشار:1996
تعداد صفحه ترجمه:6
تعداد صفحه فایل انگلیسی:9
موضوع انگلیسی :STRUCTURE AND PROPERTIES OF CAST IRON PREFORMS
OF PISTON RINGS
موضوع فارسی:دانلود ترجمه مقاله ساختار و خواص رینک پیستون ساخته شده از چدن
چکیده انگلیسی:Before 1986 piston rings for VAZ engines were manufactured
by the Michurinsk Plant of Automatic Equipment. Upper
compression rings were produced from high-strength cast
iron with spheroidal graphite, and oil-control rings and lower
compression rings were produced from gray cast iron. In both
cases individual preforms were used for each ring.
The central zone of the cross section of upper compression
rings often exhibited a streak loose shrinkage structure.
The structure of the rings was nonuniform with a variable
content of ledeburite, pearlite, and ferrite. The structure of
oil-control and lower compression rings contained coarse rosette
graphite and often an elevated amount of ferrite. Thus,
the rings had unstable micro- and macrostructures and mechanical
properties. Over 20% of the cast preforms did not
correspond to the standard requirements on the quality of the
material and the parts. The use of such piston rings caused
scoring, increased the consumption of oil, and ultimately decreased
the service life of the parts